Abstract: After formulation research of nanosized fuse2p romoting adhesives of super2low2temperature ceramics glaze, operation conditions and flowability of glaze slurry as well as the dependency of glaze weight on water con2 centration and adhesives content were investigated. Pb and Cd dissolubility of p roduct ceramics was evaluated. TEM, X2Ray diffraction and N2 adsorp tion were used to characterize nanoparticle silica, which is the main composi2 tion of the nanosized fuse2p romoting adhesives. Results indicated that nanosized silica is amorphous powder. Con2 trollable region of glaze water content for so p repared fuse2p romoting adhesives of“China2Red”glaze was between 50. 2 wt% to 51. 8 wt% , which iswider than that of JohnsonMatthey Coporation of England. In this region, glaze weight of single Langwine bottle (500 g volume) will be in a region of 4. 25 to 5. 00 gram. So p repared glaze slur2 ry possessed accep table flowability and Thixotropy. Pb and Cd dissolubility of p roduct ceramicsmeets the require2 ment of national standards.